A novel technique to prepare LiNbO3 at low temperature

Fresh niobium hydroxide was first precipitated from NbF₅ solution using an aqueous ammonium hydroxide under basic conditions. Then a simple procedure of mixing lithium and niobium hydroxides together and heating at a low temperature (400 °C) produced pure ultrafine single phase LiNbO₃ (LN). In the literature, this is the lowest temperature so far reported on the formation of LN. The phase content and lattice parameters are determined by X-ray diffraction (XRD). The average particle size and morphology were studied by transmission electron microscopy (TEM).     

Effect of C/Ti ratio on the laser ignited self-propagating high-temperature synthesis reaction of Al-Ti-C system for fabricating TiC/Al composites

TiC/Al composite was successfully synthesized utilizing laser ignited self-propagating high-temperature synthesis (SHS) of Al-C-Ti system with the different C/Ti molar ratio. When the molar ratio of C to Ti is below 1:1 in the starting materials, in addition to fine TiC particulates, a large amount of Al₃Ti phase was found in the composites; however, when the molar ratio of C to Ti is 1:1 in the starting materials, the Al₃Ti phase was almost completely eliminated and the distribution of TiC particulates generally appeared to be more homogeneous throughout the products synthesized.     

Formation of mushroom-like ZnO microcrystals through a solution calcination process

Mushroom-like ZnO microcrystals have been prepared via a solution calcination route, using Zn(NO₃)₂ as Zn source in the absence of any surfactants, templates or catalysts. This is the first example to prepare mushroom-like crystals as semiconductors, which are expected to show particular physical properties. The ZnO products were investigated by X-ray powder diffraction (XRD), scanning electron microscopy (SEM), Raman spectroscopy and photoluminescence (PL) spectrum measurements. A suitable concentration of Zn(NO₃)₂ solution was important for the growth of the mushroom-like products. The reported synthetic procedure is straightforward and inexpensive, and thus can be readily adopted to produce large quantities of mushroom-like ZnO microcrystals.     

Characterization of two-phase nickel aluminides produced by pressure-assisted combustion synthesis

Two-phase (B2+L1₂) nickel aluminide intermetallic compounds were synthesized by the pressure-assisted volume combustion synthesis (CS). The production and characterization of the samples containing NiAl+Ni₃Al were investigated. Aluminum (99% pure, 15 μm) and carbonyl nickel (99.8 pure, 4-7 μm) powders were used. The production of intermetallic compound was carried out at 1050 °C under 150 MPa uniaxial pressure in open air atmosphere in an electrical resistance furnace for 60 min. The formation temperature of intermetallic compound was determined by differential scanning calorimeter (DSC) analysis, and exothermic temperature of powder mixture was determined as 653 °C. The characterization of samples was confirmed by optical microscope, SEM and XRD analysis. It was observed that the structure of compound has very low porosity and the formation of NiAl was completed successfully. The relative density of test materials measured according to Archimedes’ principle was 98.04%. The microhardness of test materials was about 351 HVN₁.     

醋酸钾催化合成肉桂酸

对用醋酸钾作催化剂，以苯甲醛和醋酸酐为原料，通过Perkin反应制备肉桂酸进行了研究，经正交试验得出反应的最佳工艺条件：苯甲醛／醋酸酐摩尔比1：3，催化剂用量6g，反应时间2h，反应产率48．59％。     

稀疏阵列天线综合的遗传算法优化

通过遗传算法优化选择常规满阵中一定比例的工作单元,使阵列在欠饱和状态下达到窄波束低副瓣的要求。以单元的工作状态和激励幅度为优化参量,波束宽度和副瓣电平为适值函数,通过适值缩放和多种群进化竞争使遗传进化稳定地收敛到全局最优。详细分析了稀疏阵的单元布局、稀疏率及单元激励对优化阵列特性的影响。     

机械臂的动态混合控制

本文研究当机械臂的终端受有约束时的控制问题,其中心内容是给出“任务规范投影算子”的概念,利用它首先将机械臂的动态方程解耦为两组方程,它们分别描述了运动与约束力,在此基础上给出了机械臂的控制律,使闭环系统跟踪期望的速度与约束力。     

Ni的添加对TiB2-CU基复合材料微观组织的影响

利用燃烧合成工艺原位合成了TiB2-Cu基复合材料，为了改善TiB2陶瓷和Cu基体的润湿性，将金属Ni作为合金化元素加入到TiB2-Cu复合材料。通过XRD，SEM，EPMA和TEM等检测手段对金属Ni的添加对TiB2-Cu基复合材料微观组织的影响进行了研究。结果表明，含Ni复合材料的金属粘结相的面间距比不含Ni时Cu的面间距均有不同程度的减小；Ni加入后，TiB2-Cu-Ni复合材料的组织较TiB2-Cu复合材料更加致密，但陶瓷颗粒尺寸却大于TiB2-Cu复合材料的颗粒尺寸；Ni的加入降低了复合材料的导热率和冷却速度，使得部分TiB2陶瓷颗粒有足够的时间长成棒状，同时造成TiB2陶瓷颗粒间形成更多的烧结颈；Ni的加入也改善了陶瓷与金属粘结相之间的润湿性，使陶瓷相与金属粘结相的界面结合牢固，看不到TiB2-Cu复合材料中界面脱开的现象。金属Ni的添加有利于改善TiB2-Cu基复合材料的微观组织，进而利于复合材料的致密化。